Ive had some powder/flakes in my oil since 20K(50K now) Im pretty sure its a bit of bearing material getting beaten out during detonation, Im sure if I tore my motor down I would be down to the bronze on a couple of spots on the rod bearings
this is an exagerated example, but after heavy use the babbit material will seperate from the bronze substrate.